EM - Escola de Minas
URI permanente desta comunidadehttp://www.hml.repositorio.ufop.br/handle/123456789/6
Notícias
A Escola de Minas de Ouro Preto foi fundada pelo cientista Claude Henri Gorceix e inaugurada em 12 de outubro de 1876.
Navegar
3 resultados
Resultados da Pesquisa
Item Influence of cooling methods on the residual mechanical behavior of fire-exposed concrete : an experimental study.(2019) Carvalho, Espedito Felipe Teixeira de; Silva Neto, João Trajano da; Soares Junior, Paulo Roberto Ribeiro; Maciel, Priscila de Souza; Fransozo, Hélder Luís; Bezerra, Augusto Cesar da Silva; Gouveia, Antônio Maria Claret deThis work reports the main conclusions of a study on the mechanical behavior of concrete under ISO 834 fire with different cooling methods. The aim of this research was to provide reliable data for the analysis of structures damaged by fire. The experimental program used cylindrical concrete test specimens subjected to ISO 834 heating in a furnace up to maximum gas temperatures of 400, 500, 600, 700, and 800 ◦C. The compressive strength was measured in three situations: (a) at the different temperature levels reached in the furnace; (b) after a natural cooling process; and (c) after aspersion with water at ambient temperature. The results indicate that the concrete residual compressive strength is fairly dependent on the maximum temperature reached in the furnace and revealed that concrete of a lower strength preserved relatively higher levels of strength. The cooling method significantly influenced the strength, albeit at a lower intensity. In all cases, the residual strength remained in the range of 38% to 67% of the strength at ambient temperature. The statistical analysis showed that the data obtained by the experimental program are significant and confirmed the influence of the conditions imposed on the residual strength.Item Influence of cooling methods on the residual mechanical behavior of fire-exposed concrete : an experimental study.(2019) Carvalho, Espedito Felipe Teixeira de; Silva Neto, João Trajano da; Soares Junior, Paulo Roberto Ribeiro; Maciel, Priscila de Souza; Fransozo, Hélder Luís; Bezerra, Augusto Cesar da Silva; Gouveia, Alberto Frederico Vieira de SousaThis work reports the main conclusions of a study on the mechanical behavior of concrete under ISO 834 fire with different cooling methods. The aim of this research was to provide reliable data for the analysis of structures damaged by fire. The experimental program used cylindrical concrete test specimens subjected to ISO 834 heating in a furnace up to maximum gas temperatures of 400, 500, 600, 700, and 800 °C. The compressive strength was measured in three situations: (a) at the different temperature levels reached in the furnace; (b) after a natural cooling process; and (c) after aspersion with water at ambient temperature. The results indicate that the concrete residual compressive strength is fairly dependent on the maximum temperature reached in the furnace and revealed that concrete of a lower strength preserved relatively higher levels of strength. The cooling method significantly influenced the strength, albeit at a lower intensity. In all cases, the residual strength remained in the range of 38% to 67% of the strength at ambient temperature. The statistical analysis showed that the data obtained by the experimental program are significant and confirmed the influence of the conditions imposed on the residual strength.Item Avaliação de desempenho de habitações de baixo custo estruturadas em aço.(2003) Fransozo, Hélder Luís; Souza, Henor Artur de; Freitas, Marcílio Sousa da RochaO aço está se tornando um elemento construtivo muito importante na construção civil brasileira. Isto se deve às vantagens que ele apresenta, tais como: alta eficiência construtiva, alívio das fundações em relação a estruturas feitas de concreto, redução do tempo de construção e do volume de desperdícios em obra, e as diversas possibilidades arquitetônicas oferecidas. Somando todas essas vantagens a um projeto que integre, de maneira eficaz, os vários sistemas associados ao aço, as edificações em estrutura metálica têm a possibilidade de conduzir a empreendimentos eficientes e economicamente viáveis. Dentre os sistemas complementares em uma edificação metálica, um dos mais importantes é o sistema de fechamentos, para o qual o mercado brasileiro já apresenta diversos tipos de painéis industrializados. Para que a escolha dos fechamentos represente uma solução eficiente, é necessário que se levem em conta tanto os detalhes construtivos como o bom desempenho no que diz respeito ao conforto ambiental. Com o objetivo de avaliar o desempenho térmico de vários sistemas de fechamento existentes no mercado brasileiro e da construção estruturada em aço, o presente trabalho apresenta uma avaliação, realizada através de simulações computacionais, do desempenho térmico de edificações em estrutura metálica populares e/ou de pequeno porte, para várias regiões climáticas do país. Neste estudo, são levados em consideração os princípios da arquitetura climática de regiões diferentes, as propriedades dos materiais, bem como as fontes internas e externas de calor em relação ao ambiente analisado. As simulações computacionais são realizadas utilizando o Programa ESP-r. Os resultados obtidos permitirão determinar qual o tipo de elemento de fechamento mais adequado para a obtenção da condição de conforto térmico para os ocupantes dessas edificações.